Tungsten copper bar
1.Length: <300mm
2.Width:<200mm
3.Thickness:>1mm
4.Tungsten content: 55%-90%W
5.Surface: Machining surface, Ground surface
6.Certificate: ISO9001:2008
7.Specifications of Tungsten Copper Alloy:
| Item No. |
Chemical Composition % |
Mechanical properties |
| Cu |
Impurity |
W |
Density
(g/cm3 ) |
Hardness
HB |
RES( cm) |
Conductivity
IACS/ % |
TRS/ Mpa |
| CuW(50) |
50+2.0 |
0.5 |
Balance |
11.85 |
115 |
3.2 |
54 |
|
| CuW(55) |
45+ 2.0 |
0.5 |
Balance |
12.30 |
125 |
3.5 |
49 |
|
| CuW(60) |
40+2.0 |
0.5 |
Balance |
12.75 |
140 |
3.7 |
47 |
|
| CuW(65) |
35+2.0 |
0.5 |
Balance |
13.30 |
155 |
3.9 |
44 |
|
| CuW(70) |
30+2.0 |
0.5 |
Balance |
13.80 |
175 |
4.1 |
42 |
790 |
| CuW(75) |
25+2.0 |
0.5 |
Balance |
14.50 |
195 |
4.5 |
38 |
885 |
| CuW(80) |
20+2.0 |
0.5 |
Balance |
15.15 |
220 |
5.0 |
34 |
980 |
| CuW(85) |
15+2.0 |
0.5 |
Balance |
15.90 |
240 |
5.7 |
30 |
1080 |
| CuW(90) |
10+2.0 |
0.5 |
Balance |
16.75 |
260 |
6.5 |
27 |
1160 |
| Type |
Length (mm) |
Width (mm) |
Thickness (mm) |
Diameter (mm) |
| Tungsten copper rod |
2~500 |
----- |
----- |
2~320 |
| Tungsten copper tube |
<300 |
|
|
2~290 |
| Tungsten copper bar |
<300 |
<200 |
>1mm |
|
| Tungsten copper plate |
10~300 |
10~300 |
2~200 |
----- |
| Special shape: |
<300 |
<190 |
|
|
| Other products |
Cube, ring, block, tungsten copper electrode, other shaped products are custo |
8.Applications:
Tungsten alloy bar are widely used to make Grid siderod, Lead, Support, Electrode for the Gas discharge lamp.Copper tungsten alloy is used when
a product or part needs to have a high heat resistance, low thermal expansion and high electrical or thermal conductivity. Tungsten copper alloy
is used to make engines and electrical devices. It is also used in the fields of aviation and spaceflight. Electrodes,
refractory parts, heat sinks, rocket parts and electrical contacts are all made out of WCu alloy.
The alloy is also made into sheet metal, tubing and plate metal. WCu alloy is used to make contacts for both high and low voltage electrical devices,
and for high speed steel devices and switches.
The Spark Erosion (EDM) process calls for copper tungsten. Usually this process is used with graphite, but tungsten has a high melting point.
This allows the CuW electrodes to have a longer service life than the graphite electrodes. This is crucial when the electrodes have been
processed with complex machining. Since the electrodes are susceptible to wear the electrodes provide more geometrical
accuracy than the other electrodes. These properties also let the rods and tubes manufactured for
spark erosion be made smaller in diameter and have a longer length since the material is less likely to chip and warp.
|
|
Tungsten copper rods/bars/sheets/plates with high quality from Zhuzhou China Images
|